Dry film thickness gauge with fixed and cable sensor
Article No. 3676
byko-test 9500 Basic
Basic DFT gauge Fe/NFe Substrates with fixed and cable sensor
- For measurement on ferrous and non-ferrous substrates
- Total Memory 10.000 readings
- IP 65 dust and splash water protection
- USB connectivity and PC software
- ISO 17025 certificate included
Features
The byko-test 9500 dry film thickness gauge has a modular design to accommodate a wide range of applications.
- Easy to use operator menu
- Temperature compensation directly in the sensor
- Precise measurements even on curvatures and small parts
- Easy adjustment on rough, smooth or curved substrates
- 61mm (2.4”) color display, resistant against scratches and chemicals (Level H6)
- Stainless steel probe with dust protection membrane (IP65)
- Optimal readability of flip display even in direct sunlight, brightness can be adjusted automatically or manually
- Intuitive menu guidance for the gauge and software, report by 3 clicks
- Freely assignable key for individual fast access
- Simple and fast creation of documentation and reports
- Multiple languages
Technical Attributes
-
- Measuring Range Mils / µm
- 0 - 118 mil 0 - 3,000 µm
-
- Full Scale Calibration Range Mils/ µm
- -
-
- Measuring Range
- 0 - 3000 µm
-
- Measuring Range
- 0 - 118 mil
-
- Accuracy
-
Fe: 0-2000µm: ± (1 μm + 2 %)
NFe: 0-2000µm: ± (2 μm + 2 %)
Fe & NFe > 2000µm ± 3 %
-
- Measuring area, min.
- 14.5 mm ø
-
- Measuring area, min.
- 0.6 in ø
-
- Minimum Curvature
- Fe (NFe) convex: 4 mm (30mm) with 2-point-adjustment, zero and 250 μm on original substrate 6 mm (50 mm) with zero adjustment on original substrate
-
- Minimum Curvature
- Fe (NFe) convex: 0.16 in (1.2 in) with 2-point-adjustment, zero and 9 mils on original substrate 0.24 in (2 in) with zero adjustment on original substrate
-
- Minimum substrate thickness
- Fe (NFe) 25 μm (20 µm) with 2-point-adjustment, zero and 250 μm on original substrate 100 μm (50 µm) with zero adjustment on original substrate
-
- Minimum substrate thickness
- Fe (NFe) 1 mil (0.8 mils) with 2-point-adjustment, zero and 9 mils on original substrate 4 mils (2 mils) with zero adjustment on original substrate
-
- Resolution
- Adjustable: 0,1 µm (0,1 mils) or 0,01 µm (0,01 mils)
-
- Interface
- USB
-
- Power supply
- 2 x AA Batteries 1.5 V Alkali, or rechargeable AA 1.2 V
-
- Weight
- 0.27 kg
-
- Operating temperature
- -20 - 70 °C
-
- Storing temperature
- -20 - 70 °C
-
- Operating temperature
- -4 - 158 °F
-
- Storing temperature
- -4 - 158 °F
-
- Dimensions: L x W x H
- 16 x 6.8 x 3.8 cm
-
- Dimensions: L x W x H
- 6.3 x 2.7 x 1.5 in
Technical Specifications
Thickness Measurement
General
Standards
Delivery Content
byko-test 9500 Basic w/o probe
Dual Probe 3mm for byko-test 9500, ISO 17025 (3678)
Extension cable for 5500/9500 DFT gauge model (15077)
Fe- and NFe- Reference Plate w/2 Foils (15078)
2 Mignon batteries 1,5 V (AA) alkaline
Certificate
Operating Manual
Dual Probe 3mm for byko-test 9500, ISO 17025 (3678)
Extension cable for 5500/9500 DFT gauge model (15077)
Fe- and NFe- Reference Plate w/2 Foils (15078)
2 Mignon batteries 1,5 V (AA) alkaline
Certificate
Operating Manual
Downloads
Product Brochure
Safety Instructions
Short Instructions
Knowledge
Film thickness
For all requirements associated with a coating, there is an optimal layer thickness to ensure good flow and leveling, gloss, optimal color uniformity and opacity as well as good protection against environmental influences and corrosion. If the layer thickness is too high, mechanical-technological properties such as mandrel bending tests, stone impact tests and ball impact tests deteriorate, and the cost-effectiveness of the painting process also decreases. For this reason, layer thicknesses are worked out and specified by the paint supplier and quality assurance. These must be regularly checked and documented.
Read moreAccessories
Other ALTANA divisions
A member of